Tra-bond 2151, Bipax (3g)

$16.59 Buy It Now or Best Offer 1d 9h, $6.99 Shipping, eBay Money Back Guarantee

Seller: raytum (51) 100%, Location: Sterling, Virginia, Ships to: US, Item: 323996378200 TRA-BOND 2151 is a thixotropic, two-part adhesive that develops strong, durable high-impact bonds at room temperature, improving heat transfer while maintaining electrical insulation. TRA-BOND 2151 bonds offer resistance to salts, mild acids and alkalis, petroleum products, lubricating oils and alcohol. TRA-BOND 2151 passes NASA out gassing standards. TYPICAL PROPERTIES OF UNCURED MATERIAL Mixed Properties: Color: Blue Viscosity @ 25°C,mPa∙s (cP): rv#7, 10rpm 40,000 Thixotropic Index (5/5 rpm) 1.7 Specific Gravity, g/cm³ 2,300 Reactive solids contents, % 100 Pot life , minutes: @ 25 grams 45 @ 100 grams 35 Work Life, hours: @ 25 grams 1.5 @ 100 grams 1.25 TYPICAL CURING PERFORMANCE Cure Schedule 24 hours @ 25°C or 2 to 4 hours @ 65°C The above cure profile is a guideline recommendation. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures. TYPICAL PROPERTIES OF CURED MATERIAL Physical Properties: Coefficient of Thermal Expansion, ppm/ºC 26 Glass Transition Temperature (Tg), °C 60 Thermal Conductivity, W/(m-K) 0.95 Hardness, Shore D 90 Electrical Properties: Volume Resistivity, ohms-cm: @ 25°C 2.10×1015 @ 75°C 2.10×1015 TYPICAL PERFORMANCE OF CURED MATERIAL Lap Shear Strength : Alum to Alum: Cured@ 65°C for 2 hours N/mm² 20 (psi) (2,850) Cured@ 25°C for 24 hours N/mm² 15 (psi) (2,150) Gold to gold: Cured@ 65°C for 30 minutes N/mm² 6 (psi) (880) Tensile Strength, cured 30 min @ 65ºC N/mm² 50 (psi) (7,500) IZOD Impact Resistance : Ft. lbs/inch of notch 0.49 J/m 26 GENERAL INFORMATION For safe handling information on this product, consult the Material Safety Data Sheet,(MSDS). DIRECTIONS FOR USE Carefully clean and dry all surfaces to be bonded. Remove clamp and thoroughly mix the TRA-BOND 2151 epoxy adhesive system components in the handy BIPAX mixing-dispenser package until color is uniform throughout. Apply this completely mixed adhesive to the prepared surfaces, and gently press these surfaces together. Contact pressure is adequate for strong, reliable bonds; however, maintain contact until adhesive is completely cured. Some separation of components is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.Some ingredients in this formulation provided in BIPAX, TRA-PAX and bulk packaging may crystallize when subjected to low temperature storage. A gentle warming cycle of 52ºC for 30 minutes prior to mixing components may be necessary. Crystallized epoxy components do not react as well as liquid components and should be redissolved prior to use for best results. Condition: New, Model: Tra-bond, Country/Region of Manufacture: United States, MPN: EC1401008, Brand: Loctite

PicClick Insights PicClick Exclusive
  •  Popularity - 373 views, 2.1 views per day, 181 days on eBay. Super high amount of views. 5 sold, 45 available.
  •  Price -
  •  Seller - 51+ items sold. 0% negative feedback. Great seller with very good positive feedback and over 50 ratings.
Similar Items